A fast drying water borne anti-corrosive primer for ferrous metals. Passes 1000 hour hot salt spray test to ASTM B117 standard on suitably prepared substrates. Low odour. Non flammable. Dries to a sheen finish. Suitable for use on ferrous metals. Fast drying paint that can be applied by conventional, HVLP or airless spray equipment.
Low odour, solvent free system
Good flexibility and scratch resistance
Suitable for application by brush, roller or spray
Compliance: EU Limit value for this product (cat A/i (2010)140 g/l VOC. VOC Content less than 5g/litre.
Please refer to Material Safety Data Sheet and Technical Information Sheet prior to the use of this product. See download tab.
Application Methods: Brush (small areas only) Conventional Spray, Airless Spray
Colour Availability: Grey
Pack Size: 5 litre tins & 20 litre pails. 205 litre drums and 1000 litre IBC's to order
Drying Time @ 20ºC: Drying times will be extended at low temperatures . Do not apply when ambient temperature falls below 10ºC or relative humidity exceeds 80%.
Surface Dry @ 20ºC : 30 minutes
Hard Dry @ 20ºC: 2 hours Can be force dried @ 60 - 90ºC for 5 - 15 minutes
Dry Film Thickness: 40 -60 μ
Wet Film Thickness: 90 - 140 μ
Coverage: Approximately 7 - 11m² per 1 litre @ 25 μ DFT. Coverage can be affected by such variables as type and condition of substrate, type of application equipment and individual method of application.
Flash Point: Not applicable
VOC Content (as supplied): Max 5g /litre
Storage: Store in temperature range 5-40ºC
Thinners: Use clean cold water
Directions for Use: Ensure all surfaces are clean, dry and free from dust, grease, millscale, etc.
Stir thoroughly before use.
Apply one or more coats of the primer to acheie the desired dry film thickness.
Top Coat: For a full paint system overcoat
with Firwood 2580 -Water borne gloss paint.
Use clean cold water.
Wash application equipment immediately after use.
Please click here to download the Technical Information Sheet PDF.
Please click here to download the Material Safety Data Sheet PDF.